Aluminium Rod 1350 - 9.5 mm
This is produced with Continuous Casting and Rolling Line and aluminum ( Electrical Conductors Grade ) ingots melting, in diameter of 9.5 mm.
and produced in the form of basket weight up to 4000 kg or coils with 1000 – 2000 kg or any special weight ordered .
MECHANICAL & ELECTRICAL ANALYSIS | |||||||
|---|---|---|---|---|---|---|---|
# | Grade No | Diameter mm | Special Resistance Ω.mm2/km | Conductivity IACS% | Tensile Mpa | Elongation % | Packing Weight Kg |
1 | Grade - O | 9.5 ± 0.5 | Max 27.89 | Min 61.8 | 59-97 | 18-30 | 3500-4000 |
2 | Grade - H12 | 9.5 ± 0.5 | Max 28.03 | Min 61.5 | 83-117 | 12-24 | 3500-4000 |
3 | Grade - H14 | 9.5 ± 0.5 | Max 28.08 | Min 61.4 | 103-138 | 8-15 | 3500-4000 |
CHEMICAL ANALYSIS | |||||||
Al, min | Si, max | Fe, max | Cu, max | Mg, max | Zn, max | B, max | Va, max |
99.7 | 0.08 | 0.14 | 0.02 | 0.01 | 0.04 | 0.02 | 0.01 |
Aluminium Rod 1100 - 12 mm
Aluminum rod (12 mm) is used as a deoxygenator in the steel melt cauldron on steel industry . Production of aluminum rod (12 mm) has two cases : 1 – Coil form of 1000 – 2000 kg 2 – Granule production (chips) It has also been used as raw material for the production of various types of flat wire (aluminum belt) for use in magnets.
MECHANICAL & ELECTRICAL ANALYSIS | |||||||
|---|---|---|---|---|---|---|---|
Density (g/cm3) | 2.705 | ||||||
Diameter (mm) | 12 ± 0.5 | ||||||
Tensile (Mpa) | 100-120 | ||||||
Elongation (%) | Min 8 | ||||||
Packing type | Vertical-Coil with wooden pallet | ||||||
Packing weight (Kg) | 2000-2300 | ||||||
CHEMICAL ANALYSIS | |||||||
Al, min | Si, max | Fe, max | Cu, max | Mg, max | Zn, max | B, max | Va, max |
99.5 | 0.1 | 0.4 | 0.02 | 0.01 | 0.04 | 0.02 | 0.01 |